| Gel time | : | 15 min |
| Gel to peak exotherm | : | 18 min |
| Total time to peak exotherm | : | 28 min |
| Peak exotherm temperature | : | 174°C (345 °F) |
| Barcol hardness | : | 49 |
| Tensile strength | : | 6672 psi (469 kg/cm 2) |
| Tensile modulus | : | 73 x 10 9 pa |
| Heat distortion temperature | : | 117°C (243 °F)@ 264 psi (19 kg/cm 2) |
| Adhesive strength | : | 1958 psi (138 kg/cm 2) |
| Tensile elongation | : | 2.8% |
| Flexural strength | : | 23931 psi (1683 kg/cm 2) |
| Flexural modulus | : | 6.8 x 10 9 pa |
| Fire Resistance | Recommended Coating Thickness (I-Beam) | Product Usage Per Coating |
|---|---|---|
| 1 hour fire protection |
1.0 mm thk / 2 coatings | 800 grams / m 2 |
| 2 hours fire protection | 1.5 mm thk / 3 coatings | 800 grams / m 2 |
| 3 hours fire protection | 3.5 mm thk / 7 coatings | 800 grams / m 2 |